Evaluation of the material’s damage in gas turbine rotors by instrumented spherical indentation
Journal Title: Frattura ed Integrità Strutturale - Year 2014, Vol 8, Issue 30
Abstract
Experimental indentations are carried out on items of two different materials, taken in several location of various components from high pressure gas turbine rotor which have seen an extensive service. The components object of investigation consisted in 1st and 2nd high pressure turbine wheels made in nickel-base superalloy (Inconel 718), the spacer ring (Inconel 718) and the compressor shaft made in CrMoV low alloy steel (ASTM A471 type10). Aim of the work is to set up the capability of the instrumented spherical indentation testing system to evaluate variations in the material properties due to damage, resulting from temperature field and stresses acting on components during service. To perform this task load-indentation depth curves will be acquired in various zones of the above mentioned components. The analysis of the results has allowed to identify an energy parameter which shows a linear evolution with the mean temperature acting on the components.
Authors and Affiliations
D. Nappini, G. Zonfrillo, F. Mastromatteo, I. Giovannetti
Keywords
Related Articles
- EP ID EP132021
- DOI -
- Views 71
- Downloads 0
Numerical study of the response of dynamic parameters to defects in composite structures
The purpose of this work is to study three different models of delamination in composite plate (the free mode model, the constrained model and the contact model) and applicability of this models to the vibrational...
Use of FBG sensors for monitoring cracks of the equestrian statue of Bartolomeo Colleoni in Venice
The Bartolomeo Colleoni monument suffered for years damage from the local climate. The process of restoring the Colleoni equestrian statue, started in 2003, allowed to understand how the bronze statue was origina...
Implementation of a damage model in a finite element program for computation of structures under dynamic loading
This work is a numerical simulation of nonlinear problems of the damage process and fracture of quasi-brittle materials especially concrete. In this study, we model the macroscopic behavior of concrete material,...
Effect of flexural crack on plain concrete beam failure mechanism A numerical simulation
The flexural failure of plain concrete beam occurs along with development of flexural crack on beam. In this paper by using ABAQUS, mechanism failure of plain concrete beam under three steps have been simulat...
Crack initiation and fracture features of Fe–Co–B–Si–Nb bulk metallic glass during compression
The aim of the paper was investigation crack initiation and fracture features developed during compression of Fe-based bulk metallic glass (BMG). These Fe-based BMG has received great attention as a new class...