Experimental investigation of crack initiation and propagation in high- and gigacycle fatigue in titanium alloys by study of morphology of fracture
Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 35
Abstract
Fatigue (high- and gigacycle) crack initiation and its propagation in titanium alloys with coarse and fine grain structure are studied by fractography analysis of fracture surface. Fractured specimens were analyzed by interferometer microscope and electronic microscope to improve methods of monitoring of damage accumulation during fatigue test and verify the models for fatigue crack kinetics. Fatigue strength was estimated for high cycle fatigue (HCF) regime using the Luong method [1] by “in-situ” infrared scanning of the sample surface for the step-wise loading history for different grain size metals. Fine grain alloys demonstrated higher fatigue resistance for both HCF and gigacycle fatigue regimes. Fracture surface analysis for cylindrical samples was carried out using optical and electronic microscopy method. High resolution profilometry (interferometerprofiler New View 5010) data of fracture surface roughness allowed us to estimate scale invariance (the Hurst exponent) and to establish the existence of two characteristic areas of damage localization (different values of the Hurst exponent). Area 1 with diameter ~300 μm has the pronounced roughness and is associated with damage localization hotspot. Area 2 shows less amplitude roughness, occupies the rest fracture surface and considered as the trace of the fatigue crack path corresponding to the Paris kinetics.
Authors and Affiliations
M- Bannikov, O. Naimark, V. Oborin
Keywords
Related Articles
- EP ID EP159199
- DOI 10.3221/IGF-ESIS.35.06
- Views 42
- Downloads 0
A numerical study of squeeze-film damping in MEMS-based structures including rarefaction effects
In a variety of MEMS applications, the thin film of fluid responsible of squeeze-film damping results to be rarefied and, thus, not suitable to be modeled though the classical Navier-Stokes equation. The simplest w...
Evaluation and visualization of multiaxial stress and strain states under non-proportional loading
This paper presents a simple method of determining stresses and strains and a severity of loading history under non-proportional loadings with defining the rotation angles of the maximum principal stress and strai...
Applicazione della meccanica della frattura viscoelastica alla previsione della vita di tubi in polibutene
Il Polibutene-1 isotattico (i-PB1) è un materiale polimerico usato per la produzione di tubi per il trasporto di fluidi in pressione. In questo lavoro si sono studiati due tipi di i-PB1 prodotti da Basell che diffe...
L’infragilimento da idrogeno. Un caso di studio in una barra di comandi di un velivolo dell’aviazione generale.
La degradazione delle caratteristiche meccaniche di un materiale di impiego aeronautico ha pesanti ricadute sulla sicurezza del volo. Tale degradazione si può manifestare sia per l’effetto combinato tra l’ambiente...
Crack path for run-out specimens in fatigue tests: is it belonging to high- or very-high-cycle fatigue regime?
Fatigue tests run-out specimens up to 106 – 5x107 load cycles are used to determine the stress level named “fatigue limit”. Nevertheless, it is not clear what kind of fatigue cracking takes or will take place in t...