Fatigue properties and fracture mechanism of load carrying type fillet joints with one-sided welding
Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 35
Abstract
The structures of the hydraulic excavator and the crane have numerous one-sided welded joints. However, attachments with box like structures are difficult to weld at both sides. Therefore, high accurate evaluation method is needed. In this study, the fatigue properties and the fracture mechanism of the load carrying type fillet joints with one-sided welding were investigated experimentally to evaluate its fatigue damage with high accuracy based on the experimental results. As the results, fatigue cracks in the test piece initiated from the tip of the unwelded portion and propagated into the welding materials. Multiple welding defects were observed in the unwelded portion, but did not appear to be crack origins. Although these welding defects affected the direction of crack propagation they exerted minimal influence. The three-dimensional observations revealed that fatigue cracks initiate at an early stage of the fatigue development. We infer that the fatigue lifetime is chiefly governed by the crack propagation lifetime. Cracks were initiated at multiple sites in the test piece. As the number of cycles increased, these cracks propagated and combined. So considering the combination of cracks from multiple crack origins is important for a precise evaluation of fatigue damage.
Authors and Affiliations
Takamasa Abe, Hiroyuki Akebono, Masahiko Kato, Atsushi Sugeta
Keywords
Related Articles
- EP ID EP106777
- DOI 10.3221/IGF-ESIS.35.48
- Views 66
- Downloads 0
Near tip strain evolution of a growing fatigue crack
Near tip full-field strains in a growing fatigue crack have been studied in situ using the Digital Image Correlation (DIC) technique in a compact tension specimen of stainless steel 316L under tension-tension cycl...
Multi-parameter crack tip stress state description for estimation of fracture process zone extent in silicate composite WST specimens
For wedge splitting test specimens, the stress and displacement fields both in the vicinity and also in larger distance from the crack tip are investigated by means of numerical methods. Several variants of boundar...
Analisi termica per la valutazione del comportamento a fatica di provini soggetti a successive serie di carichi
Partendo dalla osservazione che provini precedentemente danneggiati hanno un limite di fatica differente (vedi Miner) viene esaminato il comportamento di un acciaio soggetto a serie di carichi affaticanti al fine di veri...
Process of cracking in reinforced concrete beams (simulation and experiment)
The paper presents the results of experimental and theoretical investigations of the mechanisms of crack formation in reinforced concrete beams subjected to quasi-static bending. The boundary-value problem has bee...
Design and characterization of a fractal-inspired multi-frequency piezoelectric energy converter
A promising harvesting technique, in terms of simplicity and efficiency, is the conversion of ambient kinetic energy through piezoelectric materials. This work aims to design and investigate a piezoelectric convert...