Simulation of accelerated strip cooling on the hot rolling mill run-out roller table
Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 37
Abstract
A mathematical model of the thermal state of the metal in the run-out roller table continuous wide hot strip mill. The mathematical model takes into account heat generation due to the polymorphic γ → α transformation of supercooled austenite phase state and the influence of the chemical composition of the steel on the physical properties of the metal. The model allows calculation of modes of accelerated cooling strips on run-out roller table continuous wide hot strip mill. Winding temperature calculation error does not exceed 20°C for 98.5 % of strips of low-carbon and low-alloy steels
Authors and Affiliations
U. Muhin, S. Belskij, E. Makarov, T. Koynov
Keywords
Related Articles
- EP ID EP159503
- DOI 10.3221/IGF-ESIS.37.40
- Views 72
- Downloads 0
A micromechanical four-phase model to predictthe compressive failure surface of cement concrete
In this work, a micromechanical model is used in order to predict the failure surface of cementconcrete subject to multi-axial compression. In the adopted model, the concrete material is schematised as acomposite w...
Crack tip fields and mixed mode fracture behaviour of progressively drawn pearlitic steel
This paper deals with the influence of the cold drawing process on the fracture behaviour of pearlitic steels. To this end, fracture tests under axial loading were performed on steel wires with different drawing...
Wedge splitting test method: quantification of influence of glued marble plates by two-parameter fracture mechanics
In the present paper, the well-known wedge splitting test (WST) is applied on specimens with different geometries (S= 150, 200, 300 mm) and variants of the specimens’ configurations. K-calibration (B1) and T-stre...
Hydrogen Re-Embrittlement of Aerospace grade High Strength Steels
Hydrogen Re-Embrittlement on anodically coated high strength steels is a relevant risk for aerospace structures due to the possibility of hydrogen uptake during the operative life of the components. AISI 4340...
Crack initiation and propagation paths in small diameter FSW 6082-T6 aluminium tubes under fatigue loading
This paper reports results of fatigue tests of friction stir welded (FSW) aluminium tubes. Relatively small 38 mm diameter tubes were used and hence an automated FSW process using a retracting tool was design...