Subsurface metals fatigue cracking without and with crack tip
Journal Title: Frattura ed Integrità Strutturale - Year 2013, Vol 7, Issue 25
Abstract
Very-High-Cycle-Fatigue regime for metals was considered and mechanisms of the subsurface crack origination were introduced. In many metals first step of crack origination takes place with specific area formation because of material pressing and rotation that directed to transition in any volume to material ultra-high-plasticity with nano-structure appearing. Then by the border of the nano-structure takes place volume rotation and fracture surface creates with spherical particles which usually named Fine-Granular-Area. In another case there takes place First-Smooth-Facet occurring in area of origin due to whirls appearing by the one of the slip systems under discussed the same stress-state conditions. Around Fine-Granular-Area or First-Smooth-Facet there plastic zone appeared and, then, subsurface cracking develops by the same manner as for through cracks. In was discussed quantum-mechanical nature of fatigue crack growth in accordance with Yang’s modulus quantization for low level of deformations. New simply equation was considered for describing subsurface cracking in metals out of Fine-Granular-Area or Fist-Smooth-Facet.
Authors and Affiliations
Andrey Shanyavskiy
Keywords
Related Articles
- EP ID EP98603
- DOI 10.3221/IGF-ESIS.25.06
- Views 86
- Downloads 0
Distribuzioni di tensione per intagli soggetti a torsione in condizioni elastiche ed elastoplastiche
Il lavoro riporta delle soluzioni analitiche in forma chiusa per le distribuzioni di tensione generate da intagli circonferenziali in componenti assialsimmetrici soggetti a torsione, in condizioni lineari elastiche ed el...
A review of using thermoelasticity for structural integrity assessment
The advances in the use of thermoelastic stress analysis (TSA) for fracture mechanics assessment are reviewed. The development of techniques to determine stress intensity factor is presented followed by the applica...
Sn and Ti influences on intermetallic phases damage in hot dip galvanizing
Protection against metallic materials corrosion is one of the most important means to reduce both maintenance costs and environmental impact. In the last years new studies on chemical baths compositions and fluxes...
Estimation of stepwise crack propagation in ceramic laminates with strong interfaces
During the last years many researchers put so much effort to design layered structures combining different materials in order to improve low fracture toughness and mechanical reliability of the ceramics. It has&nb...
Quality Control system for a hot-rolled metal surface
The modern ideas about of quality of products are based on the principle of the absolute satisfaction of requirements of recommendations of the buyer. A presence of surface defects of steel-smelting and rolli...