Preliminary Research on Granulation Process of Dust Waste from Reclamation Process of Moulding Sands with Furan Resin
Journal Title: Archiwum Odlewnictwa - Year 2012, Vol 12, Issue 3
Abstract
The results of investigations of the granulation process of foundry dusts generated in the dry mechanical reclamation process of used sands, where furan resins were binders are presented in the paper. Investigations concerned producing of granules of the determined dimensions and strength parameters. Granules were formed from the dusts mixture consisting in 50 mass% of dusts obtained after the reclamation of the furane sands and in 50 mass % of dusts from sands with bentonite. Dusts from the bentonite sands with water were used as a binder allowing the granulation of after reclamation dusts from the furane sands. The following parameters of the ready final product were determined: moisture content (W), shatter test of granules (Wz) performed directly after the granulation process and after 1, 3, 5, 10 days and nights of seasoning, water-resistance of granules after 24 hours of being immersed in water, surface porosity ep and volumetric porosity ev. In addition the shatter test and water-resistance of granulate dried at a temperature of 105oC were determined. Investigations were performed at the bowl angle of inclination 45o, for three rotational speeds of the bowl being: 10, 15, 20 rpm. For the speed of 10 rpm the granulation tests of dusts mixture after the preliminary mixing in the roller mixer and with the addition of water-glass in the amount of 2% in relation to the amount of dust were carried out. The obtained results indicate that the granulator allows to obtain granules from dusts originated from the reclamations of moulding sands with the furane resin with an addition of dusts from the bentonite sands processing plants.
Authors and Affiliations
J. Kamińska
Keywords
Related Articles
- EP ID EP72782
- DOI 10.2478/v10266-012-0081-2
- Views 102
- Downloads 0
Water mist effect on cooling process and microstructure of silumin
The paper presents the results of the process of crystallization and cooling of the AlSi11 silumin and temperature distribution in the wall of iron and bronze research casting die in the temperature field of 750 to 100°C...
Weld microstructure in cast AlSi9/SiC(p) metal matrix composites
Welded joint in cast AlSi9/SiC/20(p) metal matrix composite by manual TIG arc welding using AlMg5 filler metal has been described in his paper. Cooling curves have been stated, and the influence in distribution of reinfo...
Selected aspects of the piece production of iron alloy castings in terms of their environmental impact
Problems of environmental protection are nowadays one of the top priorities in a policy programme adopted by the European Community. Reducing the negative impact of the domestic foundry industry on environment should res...
Preliminary Research on Granulation Process of Dust Waste from Reclamation Process of Moulding Sands with Furan Resin
The results of investigations of the granulation process of foundry dusts generated in the dry mechanical reclamation process of used sands, where furan resins were binders are presented in the paper. Investigations conc...
Registration of melting and crystallization process of MCMgLi8Ca5 alloy with use of ATND method
Among lightweight metal alloys, magnesium is the lightest structural material with density of 1.74 g/cm3, having many attractive physical and mechanical properties combined with processing advantages. Therefore, it repre...