PREPARATION OF MAGNETIC ZR-PILLARED BENTONITE AND ITS APPLICATION IN CONGO RED REMOVAL
Journal Title: Topics in Chemical & Material Engineering (TCME) - Year 2018, Vol 1, Issue 1
Abstract
The magnetic bentonite material (Zr-B-Fe3O4) was prepared by a solvothermal reaction. The received Zr-B-Fe3O4 had the advantage of pillared bentonite and magnetic Fe3O4. It can be separated easily under an external magnetic field, due to the formation of Fe3O4 on the surface of bentonite. SEM image indicated that there were a number of mesoporous and stripped slice layers. Fe3O4 nanoparticles with a diameter of ~150 nm dispersed uniformly on the bentonite surface. Furthermore, Zr-B-Fe3O4 was used to remove Congo red dye in solution. The results showed that Zr-B-Fe3O4 could be employed as a low-cost material for removal of Congo red from aqueous solutions effectively and conveniently
Authors and Affiliations
Lian Li, Li Lv Jin, Yi Liu Yi, Min Ren Zhong, Yuan Ma Xian, Hong Lou Da Wei
EFFECT OF SINTERING TEMPERATURE AND TIME ON STRUCTURAL AND DIELECTRIC PROPERTIES OF TB-DOPED BATIO3 CERAMICS
Ba1−x/2Ti1−x/2TbxO3 (x = 0.05) ceramics (BTTb5) were prepared at Ts = 1400 °C for t = 6‒24 h and at Ts = 1300‒1480 °C for t = 24 h using the cold-pressing ceramic processing technique. All of BTTb5 ceramics satisfy EIA X...
RESEARCH ON KEY TECHNOLOGIES OF SERVICE INTELLIGENT ROBOT BASED ON INTERNET+
Service intelligent robots are getting more and more attention with the progress of society and the development of science and technology. However, the current service intelligent robots have some disadvantages, such as...
ZCu10Sn2ZnFe1.5Co1 SOLUTION TREATMENT PROCESS AND ORGANIZAT IONAL PERFORMANCE RESEARCH
The In-situ iron nanoparticle reinforced ZCu10Sn2ZnFe1.5Co1 alloy was fabricated by centrifugal casting in vacuum chamber with a medium frequency electrical furnace. The processes of solid solution of ZCu10Sn2ZnFe1.5Co1...
PARTICLE SIZE CONTROLLABLE CATIONIC WATERBORNE POLYURETHANE SIZING AGENT
A light blue transparent cationic waterborne polyurethane emulsion was prepared by self – assembled and self-emulsified technology. By changing the ratio of hydrophobic and hydrophilic raw materials, the particle size of...
EFFECT OF FABRICATION PARAMETERS AND MATERIAL FEATURES ON DIMENSIONAL ACCURACY OF FDM BUILD PARTS
This paper presents experimental investigations on influence of fabrication parameters viz., layer resolution, processing quality, fill mode and the processing material on dimensional accuracy of fused deposition modelli...