Quality of carburizers and its influence on carburization process
Journal Title: Archiwum Odlewnictwa - Year 2009, Vol 9, Issue 3
Abstract
In the papers issue of production the synthetic cast iron obtaining on the basis of only steel scrap and carburizing materials are presented. Natural graphite, synthetic graphite, anthracite, petroleum coke, foundry coke and charcoal were used to carburization. Examinations covered evaluation of used carburizers taking into account chemical composition; carbon, sulphur and nitrogen content have been analyzed. Obtained effectiveness of carburization with method of inserting carburizing material into charge in solid, were especially taken into considerations. The comparison between mechanical properties (tensile strength and hardness) of produced synthetic cast iron and cast iron obtained on the basis of pig iron have been carried out.
Authors and Affiliations
K. Janerka, D. Bartocha, J. Szajnar
Keywords
Related Articles
- EP ID EP72084
- DOI -
- Views 103
- Downloads 0
Application of microjet in heat treatment of aluminium bronzes
Mechanical properties of a CuAl10Fe4Ni4 bronze subjected to solution heat treatment and toughening were examined. In solution heat treatment, a microjet was used to raise the cooling rate. A slight increase of mechanical...
The structure of Ni–enriched Al–Ni molten alloy before solidification
The structure of Ni–based molten alloy, containing 88,02w.%Ni and dopped both with Zr (0,46w.%) and B (0,02w.%) has been studied by means of X–ray diffraction method at temperature 1500 K. Structure factor and pair corre...
Role of the preliminary heat treatment in anisothermic eutectoid change of the cast iron
Preliminary heat treatment, preceding continuous cooling of the iron casting, assumed in the research, complies with the applied in prac-tice single normalization, double normalization or normalization with slow cooling....
The influence of amperage of electric arc on microhardness in the area single and overlapping remeltings of HS 6-5-2 steel
The present thesis depicts the microhardness of HV0,065 surface layer of high speed steel HS6-5-2 remelted with the electric arc. There were different surface layer variants of remelting used – the amperage was changed f...
Effect of gas corrosion on the character of phase boundaries in Ni3Al / WC composite
In view of quite specific physico-chemical and performance properties, the composite based on an intermetallic Ni3Al compound reinforced with tungsten carbides (WC) was selected for investigations. The said composite is...