THE INFLUENCE OF ADSORPTION AND TEMPERATURE ON THE TRIBOLOGICAL PROPERTIES OF COMPOSITE COATINGS Ni-P-Al2O3
Journal Title: Tribologia - Year 2009, Vol 223, Issue 1
Abstract
This paper presents the analyses of the influence of the adsorption and temperature of a friction pair on the tribological properties of the Ni-P-Al2O3 composite coatings. The composite coatings were superimposed on steel elements, using the electroless plating technique. An electron-scanning microscope was used to analyse the topography. The topography of the coatings was imaged with a scanning electron microscope (SEM/EDS). The investigations of adsorption were realised using antiwear additives zinc dialkyldithiophosphates (ZDTPs), having two alkyl chain lengths, C4 and C12. The effect of adsorption on the composite surfaces had considerable influence on their tribological properties. Tribological tests were examined by means of a T-01M tester, functioning in the pin-on-disc (ball-disc) configuration. The tests were realised for technically dry friction and boundary lubrication in model lubricants oil bases and oil bases with 1% mass. ZDTP. The tribological tests were realised, and the analyses of the adsorption confirm that the kind of materials and working temperature in fact determined on tribological properties.<br/><br/>
Authors and Affiliations
Dariusz Ozimina, Monika Madej
Keywords
Related Articles
- EP ID EP516621
- DOI -
- Views 37
- Downloads 0
MODELLING THE EFFECT OF THE USE OF ROLLERS ON THEIR WEAR
An important factor in the proper operation of a mill is the appropriate planning conditions of exploitation rollers, because this factor is the limiting element in the production process. The article presents a set of o...
WŁAŚCIWOŚCI TRIBOLOGICZNE ŚREDNIOWĘGLOWEJ STALI PO AZOTOWANIU POŁĄCZONYM Z NASTĘPNYM UTLENIANIEM I IMPREGNACJĄ
W pracy omówiono wyniki badań właściwości tribologicznych i korozyjnych warstw wytwarzanych na powierzchni stali średniowęglowej C45 w procesie azotowania gazowego połączonym z następną obróbką – utlenianiem i impregnacj...
TRIBOLOGICAL PROPERTIES OF CAST IRON EN-GJSFP-500-7 AFTER A BURNISHING PROCESS MODIFIED BY EXPLORATION PREPARATIONS BASED ON SOLID LUBRICANT AND CHEMICAL ACTION
In the paper, the results of research on the base machine oil SN-150 and the exploitative preparations R-2000 (preparation on the basis of soft metals) and Motor LIFE (preparation using chemical actions) influence on the...
Odporność oksydacyjna i właściwości smarne stabilizowanych roślinnych baz olejowych
Zastosowanie modyfikacji procesu oksypolimeryzacji oleju roślinnego z wykorzystaniem inhibitora Irgaoxu i/lub przedmuchu mieszaniny reakcyjnej gazem inertnym miało na celu uzyskanie stabilizacji właściwości otrzymanych o...
Badania nad zastosowaniem ciągłego pomiaru konsystencji do identyfikacji efektu relaksacji naprężeń w mikrostrukturze smarów plastycznych
W artykule krótko omówiono budowę smarów plastycznych i wskazano na szczególny wpływ oddziaływań międzymolekularnych na stabilność mikrostruktury kompozycji smarowej. Zaproponowano modyfikację dotychczasowej normatywnej...