The influence of ceramic fibre on thermal expansion of moulding materials for investment casting technology
Journal Title: Archiwum Odlewnictwa - Year 2009, Vol 9, Issue 2
Abstract
The results of dilatometric measurements presented in the paper are a supplement to the investigations concerning broadening the composition of ceramic slurry intended for investment casting technology with ceramic fibre matrix. An applying of fibre material and a change of rheologic characteristics of ceramic slurry have impelled to develop the method of applying the material to the pattern sets. The technology of multi-layer spraying has been found to be the most favourable method. Partial replacing of the grain silica materials with aluminosilicate materials in the fibrous form has affected the magnitude of dimensional changes taking place during the heating process. In order to determine the magnitude of these changes, there have been prepared slurries of various fibre fraction in the matrix and their thermal expansion has been examined within the temperature range of 273-1273 K.
Authors and Affiliations
M. Nadolski, Z. Konopka, A. Zyska
Keywords
Related Articles
- EP ID EP71659
- DOI -
- Views 86
- Downloads 0
A method for determination of complete mechanical characteristics of heterogeneous-structured materials
The article outlines the possibilities to evaluate by a modified low-cycle fatigue test the quality of materials characterised by different structures and the resulting mechanical properties. The method was described by...
Ferritic-austenitic cast steel - selected problems
The author has been involved in the problems occurring in the manufacture of ferritic-austenitic cast steel castings for many years. The author’s remarks and investigation results reported in this article will enable pot...
Tribological resistance of high speed steel HS 6-5-2 remelted with electric arc
The intensity of tribological wear of the high speed steel HS 6-5-2 remelted with the GTAW method has been compared to the heat treatment steel in a conventional way. Moreover, the types of the wear appeared during the f...
Effect of alloying elements on branching of primary austenite dendrites in Ni-Mn-Cu cast iron
Within the research, determined were direction and intensity of influence of individual alloying elements on branching degree of primary austenite dendrites in austenitic cast iron Ni-Mn-Cu. 30 cast shafts dia. 20 mm wer...
Analysis of the failure causes in an element made of AlSi11Cu2(Fe) alloy
The paper presents results of research on a cross element damaged during the service, made of the casting alloy of aluminum - AlSi11Cu2(Fe) (AK132). Performed research was to explain the reasons for this damage and inclu...