THE INFLUENCE OF E-BEAM RADIATION ON PLASTIC DEFORMATION, MECHANICAL PROPERTIES AND WEAR OF THE POLYETHYLENE GUR 1050 FOR ACETABULAR CUPS
Journal Title: Tribologia - Year 2011, Vol 239, Issue 5
Abstract
The resistance of polyethylene to wear and permanent deformation influences the durability of polymer-metal kinematic systems. The recently introduced polyethylene, GUR 1050, of a molecular weight of 9.2 • 106 g/mole is intended especially for medical implants. This justifies the need for evaluating the resistance of this material to wear and deformation and for determining if its functional properties can be improved by radiation modification. Samples of the initial (base) polymer were electron-irradiated with applying an irradiation multiplication factor I = 1–6 and a dose of 26 kGy. An analysis of changes in the deformation value under the influence of operational loads has shown an increase in the polyethylene resistance to permanent deformation as a result of the irradiation applied. The improvement of mechanical properties has been confirmed in micro-indentation tests. An increase in the hardness and Young’s modulus was identified. This effect has been preserved despite an opposite trend that causes a growing level of plastic deformation of the polymer under the influence of load. Tribological tests have shown a significant increase (by ca. 4 times) in the resistance to abrasive wear of the polyethylene modified through irradiation. The significant wear reduction prognosticates a longer life of the friction couple, which will prolong the durability of acetabular cups in the human organism. The test results presented in the paper prove the effectiveness of modification through irradiation that enhances the tested functional properties proportionally to the applied dose of electron irradiation.
Authors and Affiliations
Adrian Barylski, Jerzy Cybo, Joanna Maszybrocka, Piotr Czaja
Keywords
Related Articles
- EP ID EP270609
- DOI -
- Views 56
- Downloads 0
Ciśnienie i prędkość przepływu oleju w łożysku ślizgowym przy niestacjonarnym laminarnym smarowaniu
W artykule przedstawiono wyniki rozwiązania zmodyfikowanego ciągu równań Reynoldsa opisującego laminarny niestacjonarny przepływ oleju smarującego w szczelinie smarnej poprzecznego cylindrycznego łożyska ślizgowego. Wyni...
RESEARCH OF ANTIWEAR AND ANTISEIZURE PROPERTIES OF THE GREASES USED IN ROLLING BEARINGS
Rolling bearings exist practically in all machines where elements are interacting. They often determine the machine’s reliability, and the essential role (quite often unappreciated) is played by lubricant. The lubricant...
ŻELAZNE POROWATE ŁOŻYSKA ŚLIZGOWE NASYCONE DOBRANĄ CIECZĄ JONOWĄ
W artykule przedstawiono wybrane wyniki badań porowatych łożysk ślizgowych spiekanych z proszku żelaza Höganas NC.100.24 z dodatkiem 2,5% mas. miedzi nasączonych dobranymi cieczami jonowymi na drodze kompleksowych i szcz...
Wpływ olejów smarowych na wytrzymałość zmęczeniową stopów łożyskowych
METODYCZNE ASPEKTY WYZNACZANIA KINETYCZNEGO WSPÓŁCZYNNIKA TARCIA ZIARNIAKÓW PSZENICY METODĄ RÓWNI POCHYŁEJ
Jednym z bardziej popularnych sposobów wyznaczania tzw. kinetycznego współczynnika tarcia zewnętrznego między parą ciał stałych jest metoda równi pochyłej. Niestety, manualny pomiar czasu ruchu cząstki (zazwyczaj za pomo...