The Influences of SiO2 on the Sintering Behavior and the Properties of Na+-β/β"-Al2O3 Solid Electrolyte
Journal Title: Materials Science-Medžiagotyra - Year 2019, Vol 25, Issue 3
Abstract
SiO2-doped Na+-β/β″-Al2O3 was synthesized via a solid-state reaction, and the relationship between the SiO2 content and properties of Na+-β/β″-Al2O3 was investigated. Respective specimens were doped with 0 – 5 wt.% SiO2 as a liquid phase sintering promotor and sintered. The specimens were characterized by XRD, SEM, densimeter and impedance analyzer. In the sintered samples, the phase fraction of β″-Al2O3 decreased as the SiO2 content increased, whereas the relative sintered density was enhanced with the inclusion of less than 0.7 wt.% SiO2. The relative sintered density of Na+- β/β″-Al2O3 sintered specimen with 0.7 wt.% SiO2 doping reached 99.2 % of the theoretical density and the sintered density decreased when the amount of SiO2 was larger than 1 wt.% result from excessive liquid-phase formation during sintering. Similarly, the ionic conductivity of SiO2-doped Na+-β/β″-Al2O3 was enhanced by doping with a small amount of SiO2, whereas the addition of more than 1 wt.% SiO2 negatively affected the ionic conductivity of Na+-β/β″-Al2O3 due to a decrease in the sintered density and unfavorable phase relationship.
Authors and Affiliations
Sung-Tae Lee, Dae-Han Lee, Sung-Ki Lim
Keywords
Related Articles
- EP ID EP615547
- DOI 10.5755/j01.ms.25.3.14246
- Views 46
- Downloads 0
Effect of Microstructure on the Compressive Mechanical Properties of Ti-20Zr-6.5Al-4V Alloy
The effect of microstructure on the mechanical properties of Ti-20Zr-6.5Al-4V alloy after solution and aging treatment was investigated by compression tests. The results showed that the microstructure was consisted of a...
The Effect of Cutting Parameters on Tool Wear During the Milling of Carbon Fiber Reinforced Polymer (CFRP) Composites
Reduction of machining times and optimization of cutting parameters and conditions hold great importance in machining processes. Milling is among the most important machining processes used for machining of fiber-reinfor...
The Regeneration Cycle of Cobalt Chemical Conversion Waste Liquid on Aluminum Alloys
In this research, the regeneration cycle of cobalt chemical conversion waste liquid, the effects of oxidizing agents on solution service life, and the influence of oxidizing agents on the treatment of waste liquid was st...
Fabrication and Characterization of Graphene/Epoxy Nanocomposites
Graphene with high electric and thermal conductivities has been widely used as reinforced filler. In this study, graphene loadings in the range between 0.3 and 1.0 wt.% were added to the epoxy to fabricate the nanocompos...
Tribological Behavior of Cermet Coatings Deposited from Submicron WC-10Co-4Cr Powders Using HVOF Spraying
In this paper, we prepared cermet coatings deposited from submicron WC-CoCr powders using high-velocity oxygen-fuel (HVOF) spraying process. The detailed microstructures, slurry erosion and sliding wear resistance of as-...