The investigation of NACE composition influence and testing condition on 20 steel corrosion rate and electrochemical characteristics
Journal Title: Вісник Тернопільського національного технічного університету - Year 2018, Vol 89, Issue 1
Abstract
The influence of the NACE composition solutions (NACE-1: 3% NaCl + 0.25% CH3COOH; NACE-2: 5% NaCl + 0.5% CH3COOH) on the corrosion rate and the electrochemical characteristics of 20 steel is investigated. It is determined that in the acidic NACE-1 and NACE-2 weakly environments, the test time (2...72) hours increase leads to a significant reduction of 20 steel corrosion rate. This dependence is typical for neutral and weakly acidic environments in which corrosion products are deposited on the metal surface in the form of barrier film. The difference between 20 steel corrosion rates in both NACE solutions in static and dynamic conditions is most noticeable in 24 hours. The corrosion rate in the flowing environment after 72 hours increases 7-12 times, which is caused by the acceleration of the oxygen transport to the metal surface and the barrier film blurring. The role of dissolved oxygen, as a depolarizer, is confirmed by polarization studies and gravimetric tests after oxygen removing. So, after nitrogen lancing of NACE solutions (complete removal of O2 is fixed polarographically), the steel corrosion rate was reduced by 11%. The differences between the corrosion and electrochemical characteristics of 20 steel in NACE-1 and NACE-2 (icor, id, Еcor, bc та bа) are determined the lower solubility of O2 in solutions with a NaCl concentration greater than 3%.
Authors and Affiliations
Zvenomyra Slobodyan, Lyudmila Mahlatiuk, Roma Kupovych
Keywords
Related Articles
- EP ID EP289557
- DOI 10.33108/visnyk_tntu2018.01.058
- Views 51
- Downloads 0
Numerical modeling of complex two-level masstransfer in media of microporous particles taking advantage of the Crank-Nicolson method
Numerical solution for mathematical model of two-component diffusion in catalytic porous particles media has been proposed. The work is based on the results of previously proposed bi-porous model and considers diffusion...
The influence of surface pretreatment on the quality of plasma coatings
The paper presents research in the field of ceramic coatings. In the experiment, 5 types of ceramic coatings were applied to the base material by means of water-stabilized plasma, which was non-alloy quality structural s...
Bending of the plate with a crack in presence of plastic zones at its tops
A problem of biaxial bending under distributed bending moments at infinity of isotropic plate with the straight crack and the presence at its tops of plastic zones where Trasck’s plasticity conditions are performed as a...
About short – and long – term strength of building constructions elements restored using injection technologies
The paper is devoted to the important scientific, technical and practical problems of predicting both service life time and strength of damaged structure elements over long-term operation, bearing capacity of which was r...
Determination of non-intensive light flux intensity after propagation through layered biological environment
The results of the research of the problem of determining the intensity of the light flux of low intensity after its propagation through the layered bioenvironment are given. It was defined that the transfer of radiation...