THE ROTOR BLADES HYDROABRASION CONSUMPTION OF SAND PUMP DREDGES
Journal Title: Tribologia - Year 2012, Vol 241, Issue 1
Abstract
This article presents the effect made of cast iron rotor blades hydroabrasion consumptions in sand pump dredges. The rotor made of eutectic highchromium cast iron (2.4% C; 33.9% Cr; 1.7% Ni; 1.24% Si; 1.21% Cu; 0.43% Mn). Stream and water with about 20% quartz sand produce abrasive wear of rotor blades across the surface of the blades. The abrasive wear produces shavings of alloying ferrite and fatigue cracking and crumble out M7C3 type carbides.
Authors and Affiliations
Zenon A. Opiekun, Antoni W. Orłowicz
Keywords
Related Articles
- EP ID EP270546
- DOI -
- Views 41
- Downloads 0
WPŁYW STRUKTURY GEOMETRYCZNEJ POWIERZCHNI TARCZ STALOWYCH NA TARCIE I ZUŻYCIE FRETTINGOWE
W badaniach zastosowano tester tribologiczny Optimol SRV5. Kulka ze stali 100Cr6 o twardości 60 HRC kontaktowała się z tarczą o średnicy 10 mm wykonaną ze stali 42CrMo4 o twardości 47 HRC w warunkach frettingu. Temperatu...
Analiza właściwości mechanicznych układów powłoka-podłoże z użyciem metody indentacji z wykorzystaniem wgłębników o różnej geometrii
W pracy przedstawiono wyniki testów indentacyjnych wykonanych trzema wgłębnikami o różnej geometrii wraz z ich interpretacją dla powłok TiN, CrN i a-C:H nałożonych na miękkim podłożu stalowym. Wyniki badań wskazują, że n...
AN ESTIMATION OF THE INFLUENCE OF THE SUBSTRATE PREPARATION ON TRIBOLOGICAL PROPERTIES OF NANOCERAMIC OXIDE LAYERS
The article presents the results of tribological measurements of an aluminium oxide layer, obtained on aluminium alloy substrate with different degrees of surface preparation, with a plastic material in sliding cooperati...
A COMPARISON OF WEAR OF PLOUGH CHISELS MADE OF DIFFERENT MATERIALS AND AFTER PAD WELDING
The paper presents quantitative results of mass wear of plough chisels working in soil made of various steel types and subjected to pad welding. The research was carried out in real field conditions on soils with similar...
MATERIAL-ENERGY FORMING PRINCIPLES FOR METAL-POLYMER FRICTION PAIRS CHARACTERISATION
The paper presents a new method for increasing of service life of the metal-polymer friction pair. The investigation of the processes occurring in polymer/metal friction pairs proves that the interaction of thin polymer...