TRIBOLOGICAL PROPERTIES OF CRC+CRN TYPE HYBRID LAYERS PRODUCED IN COMBINED VACUUM CHROMIZING PROCESS AND PVD TREATMENT
Journal Title: Tribologia - Year 2011, Vol 239, Issue 5
Abstract
Tribological properties of the CrC+CrN type hybrid layers, produced on X210Cr12 steel in vacuum chromizing process combined with arc evaporation PVD treatment, have been investigated. A comparison of the CrC+CrN type hybrid layers with the CrC single carbide layers, produced on steel surface without CrN coating, has been performed. Tribological properties of the layers were performed by means of taper-three rolls test. It has been proved, that the wear resistance by friction of hybrid CrC+CrN type layers is above two times higher, than that for the single CrC carbide layers.
Authors and Affiliations
Ewa Kasprzycka, Mariusz Koprowski, Jerzy Bielanik, Sławomir Pilarczyk, Bogdan Bogdański, Iwona Bauer
Keywords
Related Articles
- EP ID EP270997
- DOI -
- Views 36
- Downloads 0
Polietery silikonowe jako efektywne dodatki modyfikujące właściwości smarne wody
STEEL WEAR RESISTANCE 100CrMnSi6-4 AFTER ABLATION LASER TEXTURE
We analysed the results of tribological laboratory model tests, including measurements of temperature, friction force, and wear, in the model friction for samples made of 100CrMnSi6-4 steel. Measurements were made using...
Właściwości tribologiczne warstw hybrydowych typu CRC+CRN wytwarzanych przez połączenie procesu chromowania próżniowego z obróbką PVD
W pracy omówiono wyniki badań dotyczących właściwości tribologicznych warstw hybrydowych typu CrC+CrN wytwarzanych na powierzchni stali narzędziowej X210Cr12 w procesach chromowania próżniowego połączonych z obróbką PVD,...
MODIFYING THE OPERATING CONDITIONS OF FRICTION PAIRS WITH SOLID LUBRICANT BASED ADDITIVES
The article presents the results of tests into the application of additives based on solid lubricants of copper, lead, and molybdenum disulphide to AN68 and CE / SF SAE 15W/40 lubricating oils. The test results were coll...
THE EVALUATION OF THE ABRASIVE WEAR OF THE TI13Nb13ZR ALLOY IMPLANTED BY NITROGEN IONS FOR FRICTION COMPONENTS OF THE HIP JOINT ENDOPROSTHESES
Due to social needs, and especially the growing demand for the hip and knee prostheses and taking into account the fact that the tribological processes play a leading role in the loss of the stability of orthopaedic pros...