TRIBOLOGICAL PROPERTIES OF MEDIUM-CARBON STEEL AFTER NITRIDING COMBINED WITH SUBSEQUENT OXIDATION AND IMPREGNATION
Journal Title: Tribologia - Year 2019, Vol 283, Issue 1
Abstract
The paper presents the results of examinations of tribological and corrosion properties of the layers produced on a C45 medium-carbon steel surface in the gas nitriding process combined with subsequent treatment – oxidation and impregnation of corrosion inhibitor. Investigations of the microstructure of these layers and their phase composition were carried out. Hardness of the layers was measured by Vickers method. Tribological properties (linear wear) of the layers were performed by means of the three-cylinder-cone method. Resistance to corrosion was determined by electrochemical methods. The investigations showed that the linear wear of the C45 steel samples with the layers produced in the combined processes of nitriding with subsequent oxidation and impregnation was smaller than that of steel samples without layers. Moreover, the corrosion resistance of these layers in aggressive solutions containing chloride ions was very good.<br/><br/>
Authors and Affiliations
Ewa KASPRZYCKA, Bogdan BOGDAŃSKI, Piotr DĄBROWSKI
Keywords
Related Articles
- EP ID EP519223
- DOI 10.5604/01.3001.0013.1430
- Views 42
- Downloads 0
Analiza naprężeń w ceramicznych elementach tocznych
Materiały ceramiczne od kilkunastu lat znajdują coraz większe zastosowanie w technice. Wynika to z charakterystycznych właściwości materiałów ceramicznych takich, jak duża twardość, odporność na korozję, możliwość stosow...
THE EFFECT OF LUBRICATION ON SURFACE ROUGHNESS CHANGE OF ROLLING BEARING ELEMENTS
The paper considers the problem of surface layer change during work. The recent studies of changes in roughness structure of bearing elements surface are the result of work on the STBL-02 tester (where the friction pair...
TRIBOLOGICAL PROPERTIES OF NICKEL ELECTROLITYCAL ALLOYS AFTER HEAT TREATMENT
This paper describes the tribological properties (linear wear) of the electrolytic coatings containing nickel alloys, Ni-Mo and Ni-W, which contain carbides forming elements. These coatings were also subjected to heat tr...
WŁAŚCIWOŚCI TRIBOLOGICZNE ŚREDNIOWĘGLOWEJ STALI PO AZOTOWANIU POŁĄCZONYM Z NASTĘPNYM UTLENIANIEM I IMPREGNACJĄ
W pracy omówiono wyniki badań właściwości tribologicznych i korozyjnych warstw wytwarzanych na powierzchni stali średniowęglowej C45 w procesie azotowania gazowego połączonym z następną obróbką – utlenianiem i impregnacj...
WPŁYW SIŁ TARCIA NA PROPAGACJE FAL WZDŁUŻNYCH W ZABLOKOWANEJ W ODWIERCIE KOLUMNIE RUR WIERTNICZYCH
W artykule przedstawiono model matematyczny i opracowano program komputerowy do analizy procesów dynamicznych, zachodzących w zablokowanej w odwiercie kolumnie rur wiertniczych podczas oswabadzania kolumny za pomocą mech...