Comparative Study of the Release of Corrosion Products from Stainless Steel Immobilization Wire and Arch Bar during Uniform Attack in Bio-fluids
Journal Title: International Journal of Research in Chemistry and Environment (IJRCE) - Year 2013, Vol 3, Issue 1
Abstract
This study compares the amount of released Co, Fe, Mn, Ni and Cr ions from stainless steel immobilization (SSI) wire and arch bar into five pseudo- and actual- bio-fluids of varying pH and chloride ion level, under various incubation time using atomic absorption spectroscopy. Co ion was not released from SSI until at 4 weeks immersion time in WBS (0.019 ± 0.001 μg/ml) and PBS (0.023 ± 0.002 μg/ml, while arch showed resistance till at 6 week of immersion. The total amount of Fe ions released into the bio-fluids by arch bar during the immersion testing was 0.360 ± 0.032 μg/mL compared to 6.462 ± 0.103 μg/mL from the immersed SSI wires (1 day to 6 weeks). However, the leaching rate of SSI wire for Fe ions was only slightly higher than of the arch wire. There is significant difference in the amount of nickel, iron and cobalt ions released from SSI wire due to decrease in pH and increased concentration of chloride ions of the immersion solutions, while the variation of pH and chloride ions of the bio-fluids had a significant effect on the amount of Ni, Mn and Cr ions released from arch bar (P ≤ 0.05). The SSI wire demonstrated a double corrosion resistance profile over that of arch wire for Co leaching, with no significant difference in the amount of Co released by SSI and arch wire for the short term test, but Fe ions released was slightly higher for SSI (P ≤ 0.05).
Authors and Affiliations
Omoniyi L. , Ekwumemgbo P. , Yahaya A.
Keywords
Related Articles
- EP ID EP151796
- DOI -
- Views 68
- Downloads 0
Solar Photocatalytic Degradation of Commercial Azo Dye Acid Orange 7 by Synthesized CaZnO2 Nanoparticle as an Effective Catalyst
The degradation of acid orange 7 (AO7) widely used as a textile dye, can be photocatalysed by CaZnO2 nanoparticle using Advanced oxidation process (AOPs). Calcium zincate nanoparticles were synthesized by solution co...
Copper Corrosion Inhibition in 1M HNO3 by 2-Thiobenzylbenzimidazole: Adsorption and Chemical Modeling of the Inhibition Efficiency
The inhibition of copper corrosion by 2-Thiobenzylbenzimidazole in 1M HNO3 was investigated by mass loss technique at different temperatures and concentrations. Langmuir adsorption isotherm and ElAwady kinetic thermody...
[b] Photocatalytic degradation of safranine O in the presence of nickel oxide[/b]
[i] Now a days, nature is suffering from a serious problem of environmental pollution. Industrial effluents are major sources causing water pollution. In the last two decades photocatalysis has been attracted the at...
[b] N-Iodosuccinimide Annulated Heterocyclization or Environment Friendly Surfactant Based Iodine Promoted Heterocyclization in Aqueous Media of a number of 1-allylhydroxy Naphthalene Precursors: Which One is Superior?[/b]
[i] A number of 2-(iodomethyl)-1,2-dihydronaphtho[2,1-b]furan derivatives have been synthesized from the corresponding allylhydroxy naphthalene precursors involving N-iodosuccinimide in acetonitrile and also by empl...
Possible Future Directions for Oceanographic Research in India
Human activities during that past two centuries have altered our environmental significantly. While much of the observed change in the mean annual global surface temperature during the last century could be explained by...