Estimation of Wear Behavior of Polyphenylene Sulphide Composites Reinforced with Glass/Carbon Fibers, Graphite and Polytetrafluoroethylene, by Pin-on-disc Test
Journal Title: Tribology in Industry - Year 2015, Vol 37, Issue 1
Abstract
Wear behavior of polyphenylene sulphide composites was investigated according to load and test speed. Two types of materials were studied: first, with 40 wt% glass fiber, and second, with 10 wt% carbon fiber, 10 wt% graphite and 10 wt%. Tribological tests were performed on the universal tribometer UMT-2, using a pin-on-disc device. The friction coefficient and wear rate for the composites were analyzed. As a result of experimental tests, it was established that polymer composite with polyphenylene sulphide matrix, carbon fibers, graphite and polytetrafluorethylene exhibit good wear behavior under operating conditions.
Authors and Affiliations
M. A. C. Besnea , D. C. Trufasu , G. Andrei , M. Bastiurea , M. S. Rodeanu
Keywords
Related Articles
- EP ID EP111248
- DOI -
- Views 86
- Downloads 0
Correlation between Surface Roughness Characteristics in CO2 Laser Cutting of Mild Steel
CO2 laser oxygen cutting of mild steel is widely used industrial application. Cut surface quality is a very important characteristic of laser cutting that ensures an advantage over other contour cutting processes. In th...
Evaluation of the Wear-Corrosion Process in Beta-Tricalcium (β-TCP) Films Obtained by Physical Vapor Deposition (PVD)
A simultaneous evaluation was done of the wear-corrosion of the coatings of beta-tricalcium phosphate on titanium (Ti) substrate deposits obtained by the magnetron sputtering technique. The characterization was developed...
Evaluation of Tribological Properties and Optimization of Electroless Ni-P-W Coating under Dry Condition using Grey Fuzzy Analysis
Electroless Ni-P-W coating has enhanced tribological properties compared to the conventional binary alloys. Hence, electroless Ni-W-P, which is a ternary alloy, is synthesized on mild steel substrates. The coatings are h...
Slurry Erosion Behavior of Destabilized and Deep Cryogenically Treated Cr-Mn-Cu White Cast Irons
The effects of destabilization treatment and destabilization followed by cryogenic treatment have been evaluated on the microstructural evolution and sand-water slurry erosion behavior of Cr-Mn-Cu white cast irons. The p...
Prediction of Coated Tools Performance in Milling Based on the Film Fatigue at Different Strain Rates
The knowledge of coated tool wear mechanisms in milling is pivotal for explaining the film failure and selecting the appropriate cutting strategy and conditions. In this paper, tool wear experiments were carried out in m...