EVALUATION OF THE FLOW ACCELERATED CORROSION OF COPPER PIPES
Journal Title: Materials Engineering - Materialove inzinierstvo (MEMI) - Year 2010, Vol 17, Issue 4
Abstract
Corrosion behavior of the Cu pipe system has been investigated by long term experiment. The two identical experimental systems were made and fulfilled by the solution of 3 % NaCl. The work medium in the first system was flowing eight hour in day and in the second the medium was stagnant. The systems were subjected eight hour in day to temperature of 80°C. After eleven month the experiment was finished and the corrosion attack and character of corrosion products in the systems have been investigated by light and SEM microscopy, EIS tests and visually too.
Authors and Affiliations
Tatiana Liptáková, Pavol Fajnor, Alexander Dodek
Keywords
Related Articles
- EP ID EP129633
- DOI -
- Views 92
- Downloads 0
USING THE VIDEOEXTENSOMETRY AND UCI - HARDNESS FOR MONITORING OF AUTOMOTIVE STEEL SHEETS
The paper deals with examination of relation between the hardness and the size of plastic zone during the tensile loading. UCI (Ultrasonic Contact Impedance) micro-hardness method was used for hardness measurements. Defo...
The investigation of the corrosion resistance of the tension clamps Skl14
At the level crossings it is possible to find the problems with the corrosion of the parts of the fastening system. These problems are especially at the rubber level crossings and in the tunnels. As a part of the thesis...
Degradation of Czechoslovak creep resistant steels after 50 years of service
Thermally loaded assemblies in the energy and chemical industries require materials that provide the necessary functional characteristics, even after very long periods of operation. For the assessment of these materials...
FATIGUE BEHAVIOR OF HOT-ROLLED STEEL INTENDED FOR COLD FORMING
In the work, there are presented measured tension and fatigue properties of eight low-carbon steels moulded in form of 20 kg ingots that were processed by controlled regime of rolling /cooling and then exposed to simulat...
QUANTITATIVE METALOGRAPHY OF HEAT TREATED ŽS6K SUPERALLOY
Alloy ŽS6K is former USSR superalloy used in DV – 2 jet engine. It is used for turbine rotor blade and whole cast small sized rotors with working temperature up to 800 ÷ 1050°C. This alloy was evaluated after annealing a...