Influence of parameters GTAW remelting process on the tribological properties of the 100Cr6 bearing steel
Journal Title: Archiwum Odlewnictwa - Year 2011, Vol 11, Issue 3
Abstract
In this work, the influence of parameters gas tungsten arc welding on the surface properties of a 100Cr6 steel was studied. Four different the current intensity has been used to remelting surface of the steel. Results of the effect of the current intensity arc electric on the microhardness, friction coefficient and wear intensity 100Cr6 steel was presented. Wear mechanisms were investigated by optical and scanning electron microscopy. Tribological test showed that the remelting with current intensity to 60A surface of the 100Cr6 leads to reduction of wear intensity in comparison to the conventional heat treatment. If treatment was made with current arc intensity - 80 A and more the wear intensity increased. During tribology tests two kinds wear material were distinguished: abrasive wear and adhesive wear.
Authors and Affiliations
W. Bochnowski
Keywords
Related Articles
- EP ID EP72292
- DOI -
- Views 109
- Downloads 0
Computer system for casting defects classification based on Polish, French and Czech specifications
Many foundries existing in Poland make casts for local and external market. It is necessary to adopt a quality control to client’s requirements. The main problem in the quality control of casting products is to detect an...
Primary and secondary crystallization of modified hypoeutectic chromium cast iron
The paper presents investigations of crystallization of modified hypoeutectic wear resistant chromium cast iron which contains carbon about 2% and chromium on three levels (12%, 18% and 25%). Three substances were applie...
Web based foundry knowledge base
The main assumptions and functions of proposed Foundry Knowledge Base (FKB) are presented in this paper. FKB is a framework for information exchange of casting products and manufacturing methods. We use CMS (Content Mana...
Registration of melting and crystallization process of MCMgLi8Ca5 alloy with use of ATND method
Among lightweight metal alloys, magnesium is the lightest structural material with density of 1.74 g/cm3, having many attractive physical and mechanical properties combined with processing advantages. Therefore, it repre...
Influence of selected modifiers on crystallization curve of chromium cast iron
In article was introduced the results of investigations of modified chromium cast iron crystallization process. It the cast iron about composition of basic elements C = 2,8 % and Cr = 18% was modified with five substance...