EFFECTIVNESS OF THE FATIGUE CRITERIA FOR COMBINED BENDING – TORSION LOADING
Journal Title: Materials Engineering - Materialove inzinierstvo (MEMI) - Year 2010, Vol 17, Issue 4
Abstract
Most of mechanical components in the engineering are frequently subjected to combined loading, which can lead to sudden fatigue failure. In present work the fatigue life of plasma-nitrided and virgin specimens is studied. Specimens made of low-alloy high-strength steel. Specimens were subjected to an in-phase combined bending-torsion loading. The plasma-nitrided specimens have significantly improved fatigue resistance. The most relevant goal of this paper is to verify the efficiency of classical and advanced stress based multiaxial criteria. The criterion proposed by McDiarmid was found to be the most precise in the fatigue life prediction for virgin specimens. On the other hand, the Matake criterion was the most successful for nitrided specimens.
Authors and Affiliations
Štepán Major
Keywords
Related Articles
- EP ID EP113744
- DOI -
- Views 105
- Downloads 0
MICROSTRUCTURE AND FRACTOGRAPHIC ANALYSIS OF DAMAGE REASONS OF COGWHEEL
The article provides an analysis of the damaged cogwheel, which was used as the drive wheel (pinion) in the steering gear box of the construction machine. The degradation of the cogwheel arose during the warranty period,...
NODULAR CAST IRON FATIGUE LIFETIME IN CYCLIC PLANE BENDING
The fatigue behavior of a component is strongly dependent also on the material and its surface condition. Therefore, the manner in which the surface is prepared during component manufacturing (surface roughness, re...
INTERNAL FRICTION USE IN MONITORING THE DEGRADATION PROCESSES IN A MATERIAL
During the measurement of the fatigue life of material, the specimen undergoes large number of stress cycles. While the observed number of cycles before failure is considered to be the most important result (often the on...
EFFECT OF SHOT PEENING ON FATIGUE PROPERTIES OF STEEL IN DIFFERENT STRUCTURAL STATES
The aim of this paper is to evaluate the effect of shot peening on fatigue properties of dual-phase steels DP 600 in received condition, as well as in condition after different regimes of heat treatment. In the work, the...
Influence of mictrostructure features on the corrosion behaviourof AZ91 alloy in chloride media
The influence of the microstructure of as-cast AZ91 magnesium alloy, which applied to solution annealing treatment and ageing treatment respectively, was evaluated in terms of its corrosion behaviour in 0.1 M NaCl soluti...