SYNTHESIS OF SULFUR-CONTAINING NITROGEN AND PHOSPHORUS FLAME RETARDANT AND ITS APPLICATION TO POLYACRYLONITRILE FIBER
Journal Title: Topics in Chemical & Material Engineering (TCME) - Year 2018, Vol 1, Issue 1
Abstract
Flame retardant ditrimethylolpropane diphosphothiourea (DDT) was synthesized by using ditrimethylolpropane(DTMP), phosphoryl chloride(POCl3) and thiourea as raw materials. Preparation of finishing agent with ethanol as solvent and used as a flame retardtant for polyacrylonitrile fiber. The effect of finishing agent solution concentration, curing temperature and curing time on flame retardancy, whiteness and breaking strength of polyacrylonitrile fiber was also discussed. The optimal synthesis conditions for DDT were determined: the finishing liquid concentration was 200g/L and baking 80℃ for 3 min. The results showed that the flame-retardant efficiency reached national standard B1 level and retained higher breaking strength and whiteness.
Authors and Affiliations
Hao Feng-Ling, Song Chuan-Jie, Liu Qun
Keywords
Related Articles
- EP ID EP414281
- DOI 10.26480/icnmim.01.2018.157.160
- Views 60
- Downloads 0
SYNTHESES OF CHIRAL N-SUBSTITUTED MALEIMIDES BEARING TWO POLYMERIZABLE GROUPS
Chiral (S)-N-maleoyl-L-leucine propargyl ester with a specific rotation of [α]435 = -27.5° and chiral (S)-N-maleoyl-L-leucine allyl ester with a specific rotation of [α]435 = -36.2°, two monomers of N-substituted maleimi...
ANAEROBIC DIGESTION OF PULP
Alkaline pulping produces a large amount of black liquor and volatile substances, such as methanol, dimethyl sulfide, terpene, ketone, etc. It can cause serious pollution of water and air. Anaerobic inhibition with ligni...
EFFECT OF MEA HOT-PRESSING ON THE PERFORMANCE OF DIRECT METHAN OL FUEL CELLS
MEA based on Nafion 115 has been prepared with GDL-based method for direct methanol fuel cell applications. The results of unit cell tests show that different temperature and pressure of hot-pressing during MEA preparati...
CONTROL ON PRODUCTION COST AND QUALITY OF CARBON FIBRE PRECURSOR
In the production of carbon fibre industry, oiling of carbon fibre precursor can impart fibre smoothness, antistatic property, and bundling property, and also allows the precursors to have sufficient high temperature res...
STUDY ON CATALYTIC ROLES OF TUNGSTEN CARBIDE NANOSPHERES FOR CH4/CO2 REFORMING OVER NI BASED CATALYSTS
In this paper, WO3 nanospheres are used carriers and Ni-WCx nanospheres are synthesized via the method of incipient impregnation and temperature programming carbonization with the content of Ni is 10%. The presence of Ni...