THE EFFECT OF OIL POCKET ARRAYS ON FRICTION COEFFICIENT
Journal Title: Tribologia - Year 2017, Vol 274, Issue 4
Abstract
Experiments were carried out using pin-on-disc tester in conformal lubricated contact conditions for different normal loads. Surface texturing was done using abrasive jet machining with the application of laser cut mask. In order to eliminate the effect of different input variables in all the experiments, pit-area ratio and sizes of oil pockets were very similar. Five types of oil pocket arrays were tested: radial, concentric, spiral, of a square arrangement, and of a random arrangement for 5% and 17% of pit-area ratio. Different dimple diameters caused various oil pocket densities. The experiments were also made for untextured polished discs. During tests, the friction force was monitored as a function of time. Before and after tests, disc surface topography was measured using a white light interferometer Talysurf CCI Lite. The beneficial effect of surface texturing was obtained for spiral arrays of dimples on disc surface. The presence of a radial array of oil pockets resulted in the worst tribological properties of tribological assemblies containing textured discs.
Authors and Affiliations
Sławomir WOŚ, Waldemar KOSZELA, Paweł PAWLUS
Keywords
Related Articles
- EP ID EP238757
- DOI 10.5604/01.3001.0010.6037
- Views 68
- Downloads 0
SCUFFING AND PITTING OF A STEEL FRICTION JOINT WITH LOW FRICTION PVD COATED ELEMENTS
The paper presents the test results of scuffing and the surface fatigue life (pitting resistance) of the modified four-ball tester friction joint, lubricated with the following oils: RL219 reference oil, PAO 8 poly-alfa-...
Wpływ nowoczesnych procesów obróbki cieplno-chemicznej i ściernej na właściwości tribologiczne powierzchni
W referacie przedstawiono właściwości warstwy wierzchniej uzyskane w procesie nawęglania próżniowego i konwencjonalnego oraz po szlifowaniu ściernicami nowej generacji. Przeanalizowano właściwości użytkowe warstwy wierzc...
INFLUENCE CuAl10Fe3Mn2 ADDITI VE ON ULTIMATE TENSILE STRENGTH AND WEAR OF Al-9%SiMg ALLOY
One of the most common castings applied in industrial production is aluminium-silicon alloy (ca. 9% Si with Mg). The Al-SiMg alloys have high corrosion resistance, high strength to weight ratio with modifications, very g...
BADANIA PORÓWNAWCZE ODPORNOŚCI NA ZUŻYCIE PRZEZ TARCIE AZOTOWANYCH I NAWĘGLANYCH STALI KONSTRUKCYJNYCH
W pracy przedstawiono wyniki badań właściwości tribologicznych azotowanych i nawęglanych stali konstrukcyjnych 18HGT i 20MnCr5. Zauważono wprost proporcjonalną zależność ich odporności na zużycie od wartości nacisków pow...
WYKORZYSTANIE ANALIZY METALOGRAFICZNEJ OKŁADZINY CIERNEJ W UKŁADZIE HAMULCOWYM DO WYZNACZENIA PROCESÓW ZUŻYWANIA TRIBOLOGICZNEGO
W pracy przedstawiono badania metalograficzne zużytych okładzin hamulcowych w różnych warunkach eksploatacji. Głównym celem niniejszej pracy jest określenie rodzajów zużycia par ciernych układów hamulcowych w określonych...