Modeling the damage of welded steel, using the GTN model
Journal Title: Materials Engineering - Materialove inzinierstvo (MEMI) - Year 2014, Vol 21, Issue 4
Abstract
The aim of our work is the modeling of the damage in the weld metal according to the finite element method and the concepts of fracture mechanics based on local approaches using the code ABAQUS calculates. The use of the Gurson-Tvergaard-Needleman model axisymmetric specimens AE type to three different zones (Base metal, molten metal and heat affected Zone) with four levels of triaxiality (AE2, AE4, AE10 and AE80), we have used to model the behavior of damage to welded steel, which is described as being due to the growth and coalescence of cavities with high rates of triaxiality
Authors and Affiliations
El-Ahmar Kadi, Benguediab Mohamed, Bouchouicha Benattou, Mazari Mohamed, Zemri Mokhtar
Keywords
Related Articles
- EP ID EP95022
- DOI -
- Views 137
- Downloads 0
CORRELATION BETWEEN HARDNESS AND TENSILE PROPERTIES IN ULTRA-HIGH STRENGTH DUAL PHASE STEELS – SHORT COMMUNICATION
The possibility to predict yield strength, strength limit, fatigue live estimation as well as other mechanical properties depending on values of materials hardness is commonly known and it is often used in practice. The...
Interaction of sub-zero treated Cr-V ledeburitic steel with alumina,100 Cr6 steel and bronze in dry sliding
The interaction of the Vanadis 6 steel, processed without/with an application of sub-zero treatment, with alumina (hard counterface), 100Cr6-ball bearing steel (counterface of an intermediate hardness) and CuSn6 (soft co...
CHOSEN PROPERTIES OF SANDWICH MATERIAL Ti-304 STAINLESS STEEL AFTER EXPLOSIVE WELDING
The work deals with evaluation of joint of stainless steel 304 SS (sheet) and commercially pure Ti both after welding explosion and followed-up annealing at 600°C/1.5h/air. The bonding line shows sinusoidal character wit...
INTERNAL FRICTION USE IN MONITORING THE DEGRADATION PROCESSES IN A MATERIAL
During the measurement of the fatigue life of material, the specimen undergoes large number of stress cycles. While the observed number of cycles before failure is considered to be the most important result (often the on...
THE STUDY OF MOLTEN ZINC INTERACTION ON THE SURFACE OF REFRACTORIES IN THE PRODUCTION OF ZINC OXIDE
This paper is closely connected with the complete process of indirect production of ZnO as well as with the problems which occur during the metallurgical process. Purity of raw materials has an important influence on the...