THE ANALYSIS OF CAUSES OF LORRY PISTON COMBUSTION ENGINE DAMAGE
Journal Title: Materials Engineering - Materialove inzinierstvo (MEMI) - Year 2012, Vol 19, Issue 2
Abstract
The article deals with analysis of causes of lorry piston combustion engine damage. For docummentation and analysis of causes was used macroscopical, microscopical and scanning electron microscopy. The analysis showed that the reason of fatal damage resides in production process of lorry combustion pistons which proved in implication of fatigue damage and subsequent burnout in two piston place.
Authors and Affiliations
Mária Štefániková, Roman Moravčík, Karin Kocúrová
Keywords
Related Articles
- EP ID EP155868
- DOI -
- Views 86
- Downloads 0
MICROSTRUCTURE AND MECHANICAL PROPERTIES DEGRADATION OF CrMo CREEP RESISTANT STEEL OPERATING UNDER CREEP CONDITIONS
In this contribution microstructure degradation of a steam tube is analysed. The tube is made of CrMo creep resistant steel and was in service under creep conditions at temperature 530°C and calculated stress level in th...
DETERMINATION OF THE OPTIMAL TEMPERING TEMPERATURE IN HARD FACING OF THE FORGING DIES
Here is analyzed selection of the optimal technology for heat treatment during the reparation of the damaged forging dies. Those tools are manufactured from alloyed tool steels for operation at elevated temperatures. Tho...
KINETICS OF HARDNESS CHANGES DURING AGE-HARDENING OF SILUMIN
Simple phenomenological description of age-hardening kinetics of supersaturated solid solution is presented using the sum of exponential functions with negative arguments containing rate constants, for whose temperature...
Study of the influence of agricultural waste on the porosity of clay brick
This paper deals with the influence of two organic residues on the porosity of clay bricks. The insulation capacity of the brick increases with increasing the porosity. Combustible organic additions are often used to for...
SELF-LUBRICATING THIN FILMS FOR TOOL STEELS
Specimens made from Vanadis 6 cold work tool steel were machined, ground, heat processed by standard regime and finally mirror polished. After that, they were layered with CrAgN. The Ag-content in the layers was chosen t...