ANALYSIS OF FRACTURE AND WEAR RESISTANCE OF ZrN COATINGS
Journal Title: Tribologia - Year 2017, Vol 273, Issue 3
Abstract
The article presents the results of mechanical and tribological studies of ZrN coatings that allowed the determination of their hardness, elasticity modulus, and scratch and wear resistance. Tests were carried out for 1, 1.4, and 2 μm thick ZrN coatings deposited on X5CrNi18-10 austenitic steel substrates by PVD technology. Hardness and Young's modulus of coatings, evaluated by nanoindentation, were within the 26–32 GPa, and 330–360 GPa ranges, respectively. Analysis of the adhesion of the coating to the substrate was carried out based on the results of the scratch test. The highest critical load values of LC1 and LC2 were measured for the 1.4 μm thick coating. Tribological tests performed using a ball-on-disc tribotester showed that the wear resistance increases with coating thickness. This was accompanied by a reduction of the coefficient of friction from 0.22 to 0.17.<br/><br/>
Authors and Affiliations
Kinga CHRONOWSKA-PRZYWARA, Marcin KOT
Keywords
Related Articles
- EP ID EP240866
- DOI 10.5604/01.3001.0010.6119
- Views 63
- Downloads 0
BADANIA WPŁYWU DŁUGOTRWAŁEGO OBCIĄŻENIA CYKLICZNEGO NA GEOMETRIĘ FOLII PODPIERAJĄCEJ GAZOWEGO ŁOŻYSKA FOLIOWEGO
W artykule opisano badania, których celem było sprawdzenie wpływu długotrwałego obciążenia tętniącego na geometrię folii podpierającej łożyska foliowego. Testom poddano folię wykonaną z jednego z najbardziej popularnych...
Wpływ ukształtowania struktury geometrycznej powierzchni stali na współczynnik tarcia statycznego współpracujących materiałów polimerowych
Ze względu na stosunkowo dużą wartość współczynnika tarcia statycznego dla par polimerowo-metalowych, opory tarcia w odniesieniu do sił bezwładności odgrywają znaczącą rolę w zapotrzebowaniu mocy i stratach energii podcz...
DEFORMATIONS AND FRACTURE ANALYSIS OF COATING-SUBSTRATE SYSTEMS USING INDENTATION METHOD WITH DIFFERENT INDENTERS
Load bearing capacity of coating-substrate systems can be found from indentation experiments using different indenter geometry by transforming the load-depth indentation diagram to stress-strain diagram. In article consi...
OPERATIONAL TESTS OF RAPESEED OIL AS AN EN-GINE LUBRICANT
In the paper, both laboratory and operational investigation methodologies of natural rapeseed oil used for petrol engine lubrication – were presented. Selected test results, included the spectroanalysis of the noise emit...
TRIBOLOGY FOR INDUSTRY AND MAN
s paper describes what determines the coefficient of friction in the general case before scuffing of machine components. The authors discussed a method for the improvement friction parameters of sports equipment, for exa...